What are the 4 determining factors of the strength of paper?

15 Apr.,2024

 

Basics of Paper Manufacturing

Paper is a thin sheet usually manufactured from cellulose pulp derived from wood and other lignocellulosic materials such as cotton, rice or wheat straw for writing, printing and packaging purposes. Some of the important production processes and properties of different kind of papers will be reviewed in this fact sheet.

 

It is believed that paper originated in China in the 2nd century as alternative writing material to silk. Production of paper was introduced to Europe in the 12th century. Almost 200 years of mechanized production of paper resulted in significant changes in information networking all over the world.

 

The first step in a typical paper manufacturing process is to produce pulp from wood chip. Softwoods, such as spruce and pine with slender, strong and elastic fibers, are most commonly used species in North America. In general, pulp, which is the raw material of paper, can be manufactured using two methods: chemical pulping or mechanical pulping.

 

The first one involves breaking down the chemical structure of lignin into a liquid using different chemicals, including sodium hydroxide and sodium sulfide. Cooking liquor is a by-product of the production, which is washed from cellulose fibers to produce pulp. Chemical pulping is used to produce higher quality paper with more expensive production cost than that of mechanical pulping.

 

Mechanical pulping can further be classified into two subgroups, namely ground pulping and thermo-mechanical pulp (TMP) that does not remove lignin from the fibers in contrast to chemical pulping. In both methods chips are simply fed into a refiner to disintegrate and to convert the material into fiber bundles. The refiners are consisted of steam-heated rotating steel discs having different types of profiles. The final product of TMP is unbleached, dark pulp with short-length fibers. The main advantage of this kind of pulp is it has a higher yield than that of chemical pulping. The second one is a more commonly used method to produce paper with low strength properties.

 

Initially, paper was made manually as single sheets until the invention of paper machine by Louis Robert in France in 1799. Figure 1 illustrates schematics of the first paper machine of Louis Robert.

 

Figure 1. Schematics of the first paper machine of Louis Robert.

 

Today, the Fourdrinier paper machine is extensively used to form the fiber mat for production of various types of papers, such as writing and drawing papers, printing and newspaper, wrapping and tissue paper, and other special papers. Typical mechanized paper production involves two main processes: the treatment of raw material, which includes converting chip into pulp, washing and bleaching, refining, beating, sizing, coloring of the fibers, and later to form paper sheet in a Fourdrinier machine.

 

For writing purposes whiteness of paper is important, therefore, pulp is bleached using mostly oxygen bleaching techniques rather than chlorine bleaching due to its high environmental pollution problem. Dark color lignin is removed during the bleaching process. Most of the strength of paper comes from hydrogen bond between fibers. Beating and refining of the pulp increase surface area of fibers so that better contact between fibers will result in higher mechanical properties of the paper.

 

A conical refiner is a widely used machine to improve pulp quality, as shown in Figure 2. Pulp flows on the screen of the Fourdrinier, and water is drained away with the help of a series of vacuum boxes and other equipment before a thin sheet of fiber mat is formed. Speed of the sheet in the machine ranges from 1,200 fpm (13.6 mph) to 5,000 fpm (56.7 mph). Once the paper web is formed in a sheet, its moisture content is reduced first using suction units, called the wet press area, and later by drum type dryers. Paper sheet continuously runs through a series of stainless steel drums heated up to 200oF (93oC) to ensure the sheet has an approximate 4-5% moisture content.

 

Figure 2. A conical refiner machine to improve pulp quality.

 

Calendering is a process to enhance both physical and mechanical properties of paper as it passes through a specially designed series of drum type rolls as a result of friction. For example, surface finish of newsprint is mainly due to calendering process. Depending on the type of paper, further finishing processes are needed. Application of coats of various types of chemicals applied to the surface of the paper make it extra shiny for special applications, such as art papers. In general, coated papers are classified into three groups: matte, semi matte and glossy.

 

Finally, the paper sheet is wound into large rolls, and then, they become ready to be shipped. Figure 3 shows the main steps of typical paper manufacturing.

 

Figure 3. The main steps of typical paper manufacturing.

 

Evaluation of Some of the Properties of Paper

Physical and mechanical properties are very important in determining overall quality of the final sheet. Tensile strength, compression strength, bending stiffness, tear and burst resistance are some of the mechanical properties of paper. Measure of the force perpendicular to the plane of the paper required to tear several pieces is used to evaluate tearing resistance. Burst strength is determined by applying pressurized air to the surface of the sheet. Stiffness is determined by bending a small sample in both directions in specially designed equipment, such as a Taber Instrument.

 

Opacity, the measurement of light passing through a sheet of paper and brightness and the percentage of light reflected from the surface of paper are two physical characteristics influencing overall printing quality. Also, texture of paper, including smoothness and finish quality, is important for many applications.

 

A sufficiently smooth surface is a basic requirement for most printing papers for proper transfer of ink. Surface smoothness of paper is well known to correlate with printability. Efforts to measure the surface smoothness can be classified into two groups: simulating the printing process by pressure on the surface and determining an original surface profile.

 

The Sheffield smoothnesstester, which measures the air leak in contact with paper under the condition of a fixed weight of measuring head, is a typical example of the first group. The stylus profilometer that falls in the second group presents an original surface profile of the paper as accurately as possible.

 

Information about Pulp and Paper Manufacturing

The Technical association of the Pulp and Paper Industry

 

Patrick, K., 1998 Primer of Pulp and Paper Making: Technologies and Production Practices.

 

Smith, M. 1997. The U.S. Paper Industry and Sustainable Production.

 

Macdonald, R.G. Ed. 1970. The Pulp and Paper Manufacture. TAPPI.

 

Volume 1. The Pulping of Wood.

 

Volume 2. Control, secondary fiber, structural board, coating.

 

Volume 3. Papermaking and Paperboard Making.


Salim Hiziroglu
FAPC Value-added Wood Products Specialist

Was this information helpful?
YESNO

What are the types of soil porosity in construction?

5 answers

In construction, soil porosity can manifest in various types. One significant type is double-porosity, where two sets of porosities with contrasting hydraulic properties coexist within the soil fabric. Another crucial aspect is the porosity of compacted soil materials, which is essential for hazardous waste disposal landfills to prevent the migration of hazardous wastes. Effective porosity, representing the portion of pore space facilitating rapid leachate transport, is a key consideration in compacted soil liners. Additionally, the composition of soil blocks in construction can lead to different types of porosity, such as packing voids, fissures, and inter-aggregate voids, influenced by the fines content and particle size distribution within the soil blocks. These various types of soil porosity play vital roles in construction projects, impacting factors like drainage, stability, and waste containment.

Does the decreasing resistivity of air increase the sound absorption properties of hemp fibers?

5 answers

The decreasing resistivity of air can indeed increase the sound absorption properties of hemp fibers. Studies have shown that the airflow resistivity and normal-incidence sound absorption coefficient of alkalized three-layered nonwoven composites, including hemp fibers, are influenced by various factors such as fiber size, porosity, treatment temperature, and concentration. Additionally, the relationships between material parameters like fiber fineness, porosity, and airflow resistivity with the sound absorption coefficient of nonwoven composites, including hemp fibers, have been investigated. It was found that air flow resistivity increases with decreasing fiber size and nonwoven porosity, impacting the sound absorption properties. Furthermore, the sound absorption coefficients of hemp fibers were found to increase with the thickness, bulk density, and air gap of the fiber assembly, indicating an improvement in sound absorption properties.

Whose young modulus is higher between jonagold apple and granny smith apple?

5 answers

The Young's modulus, a measure of stiffness, is higher in Granny Smith apples compared to Jonagold apples. This difference is attributed to the nonhomogeneity of the apple limbs, where the Young's modulus increases from the base to the tip due to variations in the cross-section composition. Additionally, the drying kinetics study reveals that Granny Smith apples exhibit better properties for drying, with lower oxidation of polyphenolic compounds and consistent drying, resulting in a higher-quality final product compared to Jonagold apples. These findings suggest that Granny Smith apples have a higher Young's modulus due to their structural characteristics and better drying properties, making them stiffer than Jonagold apples.

For Friction Stir Process, what are synonyms or other terms for "tilt angle" ?

9 answers

In the context of the Friction Stir Welding (FSW) process, the term "tilt angle" is frequently used to describe the inclination of the welding tool relative to the vertical axis of the workpiece. This parameter is crucial for controlling heat generation, material flow, and ultimately, the quality of the weld. Various studies have explored the impact of this angle on the welding process, employing different terminologies that can be considered synonyms or closely related terms to "tilt angle." 1. **Tool Tilt Angle (TTA)**: This term is directly used and is synonymous with "tilt angle," emphasizing the angle at which the tool is tilted during the welding process. It is a critical factor that influences material flow in both metallic and polymeric materials during FSW. 2. **Tool Inclination Angle**: Although not explicitly mentioned in the provided contexts, this term is conceptually similar to "tilt angle" and is used interchangeably in literature on FSW to describe the same phenomenon. 3. **Welding Tool Angle**: This term can be inferred as another way to describe the tilt angle, focusing on the orientation of the welding tool relative to the workpiece. It highlights the importance of tool positioning in achieving effective heat generation and material flow. 4. **Pin Angle**: In some contexts, especially when discussing the specifics of the tool's geometry, the angle related to the pin's orientation might be referred to in a way that encompasses the tilt angle's effects, particularly in studies focusing on the pin's role in the welding process. Each of these terms, directly or indirectly, refers to the angle at which the welding tool is positioned relative to the workpiece, affecting the welding process's thermal and mechanical dynamics. The choice of term often depends on the specific focus of the study, whether it be on the tool's design, the mechanics of the welding process, or the outcomes related to weld quality and material properties.

How improve the solubility of PVA in water?

5 answers

To enhance the solubility of Polyvinyl Alcohol (PVA) in water, several methods have been explored. One approach involves crosslinking PVA nanofibers with Hexamethylene diisocyanate (HMDI) to create stable structures with N-H and C=O groups, rendering them insoluble in water. Another method includes modifying PVA with acrylamide (AAm) to reduce stereoregularity, suppress crystallinity, and strengthen interactions with water molecules, thereby improving solubility even at low temperatures. Additionally, the use of urea in combination with methanol has been shown to generate large side groups on PVA chains, weakening hydrogen bonds, altering aggregation structures, and increasing intermolecular distance to boost water solubility by 50%. These diverse approaches offer effective strategies to enhance the solubility of PVA in water for various applications.

How does increased temperature effect building?

5 answers

Increased temperatures have a significant impact on buildings in various ways. Firstly, rising temperatures lead to higher cooling demands in buildings, resulting in increased electricity consumption and subsequent emissions from power plants, notably sulfur dioxide and nitrogen oxides, which have direct health implications. Secondly, exposure to high temperatures affects the mechanical properties of structural concrete, causing a reduction in strength, particularly in tensile and flexural strengths, with higher-grade concrete experiencing more significant strength loss. Additionally, high indoor temperatures, especially in hot-humid areas, coupled with increased humidity levels, can lead to physiological responses like elevated heart rates and discomfort among occupants, affecting thermal comfort and perceived air quality. Overall, these temperature-related factors underscore the importance of considering climate impacts on building materials, energy consumption, and indoor comfort for sustainable and resilient construction practices.

What is the optimum ranges of "tool feed Speed" within FSP to enhance the microstructure of material?

10 answers

The optimization of "tool feed speed" within Friction Stir Processing (FSP) is crucial for enhancing the microstructure of materials, as it directly influences heat generation, material flow, and mechanical properties. The studies reviewed provide insights into various materials and conditions, highlighting the importance of balancing tool feed speed with other parameters like tool rotational speed to achieve desired outcomes. For ZE41 magnesium alloy, a constant tool traversing speed of 50 mm/min was used, emphasizing the role of tool rotational speed in achieving superior mechanical properties. Similarly, in the fabrication of AA5083/Al-Fe in-situ surface composites, a tool traverse speed of 63 mm/min was part of the optimum parameter set for achieving the highest microhardness. Pure magnesium/SiC microcomposites were processed at a tool travel speed of 50 mm/min, indicating that this speed, in conjunction with appropriate rotational speeds, can lead to significant improvements in tensile strength and ductility. In contrast, the study on GFRP plates did not specify the optimal feed rates directly but indicated that varying feed rates (15 mm/min, 20 mm/min, and 25 mm/min) at a constant spindle speed were explored to enhance microstructural properties. This suggests that even within composite materials, the tool feed speed plays a significant role in determining the final material characteristics. The investigation on Al 5083 aluminium alloy highlighted that ultrarefined grains and increased microhardness were achieved at a tool rotational speed of 1000 rpm, indirectly suggesting that the tool travel speed must be adequately matched to the rotational speed to optimize microstructural refinement. Similarly, the study on as-cast Al-12.7Si alloy used a traverse speed of 150mm/min, indicating that higher speeds can be beneficial for certain aluminum alloys. In summary, while the optimum "tool feed speed" within FSP varies depending on the material and desired properties, a range between 50 mm/min to 150 mm/min is commonly explored in the literature. This range appears to balance the heat input and material flow adequately, leading to enhanced microstructures and mechanical properties across a variety of materials. However, it's crucial to consider this parameter in conjunction with tool rotational speed and other processing conditions to achieve the best results.

What is the effect of resin properties on Inter laminar shear strength of composite?

5 answers

The interlaminar shear strength (ILSS) of composites is significantly influenced by resin properties. Various studies have shown that modifying resin properties can enhance ILSS. For instance, incorporating silane coupling agents/nano-calcium carbonate into epoxy resin significantly increases ILSS, with a 36.6% improvement observed with 4 wt% nano-CaCO3 addition. Similarly, modifying EPON 862/w epoxy resin with Tetraethyl orthosilicate (TEOS) electrospun nanofibers (ENFs) enhances ILSS of glass fiber reinforced polymer composites (GFRP) by 15% with a 0.6% wt. fraction of TEOS ENFs. These findings highlight the crucial role of resin modifications in improving the interlaminar shear strength of composite materials.

What is the effect of matrix resin properties such as modulus on Inter laminar shear strength of composite?

5 answers

The mechanical properties of a composite, particularly the interlaminar shear strength (ILSS), are significantly influenced by the properties of the matrix resin. For instance, the modulus of the epoxy resin matrix plays a crucial role in determining the mechanical and interfacial properties of carbon fiber filament wound composites. Research has shown that a resin matrix with a high modulus is essential for achieving excellent mechanical properties and interfacial characteristics in resulting composites. Additionally, modifying the epoxy system with nanofibers has been found to enhance the ILSS of glass fiber reinforced polymer composites, demonstrating the impact of matrix modification on improving the ILSS of the composite. Therefore, the matrix resin's modulus is a key factor affecting the interlaminar shear strength of composites.

Does the addition of banana pseudo-stem fibers as additives can produce a water resistant and flexural concrete?

5 answers

The addition of banana pseudo-stem fibers as additives can indeed contribute to the production of water-resistant and flexural concrete. Banana fibers extracted from Musa sapientum pseudo-stems have shown promising properties, including tensile strengths of up to 743.9 MPa, moisture contents of around 10-12%, and water absorption rates reaching 140-170%. Furthermore, the incorporation of banana stem fibers in ferrocement lightweight fiber concrete has demonstrated enhancements in compressive and tensile strengths, with a notable increase of up to 83% in tensile strength when compared to concrete without fibers. Additionally, the use of banana pseudo-stem fibers in bio-fiber polymer composites has shown potential for high strength and water resistance, making them suitable for applications requiring durability and resilience to environmental conditions. Alkaline treatment of banana fibers has also been found to improve adhesion with the matrix, enhancing stiffness and potentially contributing to water resistance in composites.

How steel slag coarse aggregate is obtained?

5 answers

Steel slag coarse aggregate is obtained through various methods outlined in the research papers. The production methods include circular treatment of raw material steel slag using a spatial screening and crushing system to obtain multi-specification steel slag aggregate. Another method involves conveying steel slag raw materials to a prehomogenizing system for prehomogenization, then crushing and shaping the materials to reduce needle flake content, and finally sieving to obtain crude products of all-grade steel slag aggregates. These methods ensure the production of steel slag coarse aggregate with improved characteristics for concrete applications, surpassing the performance of natural coarse aggregates.

What are the 4 determining factors of the strength of paper?

What are the different factors that affect the tensile strength of paper?